Mechanistic Insight on the Formation of GaN:ZnO Solid Solution from Zn–Ga Layered Double Hydroxide Using Urea as the Nitriding Agent
Inorganic Chemistry 57 巻 21 号
13953-13962 頁
2018-11-05 発行
アクセス数 : 784 件
ダウンロード数 : 133 件
今月のアクセス数 : 2 件
今月のダウンロード数 : 4 件
この文献の参照には次のURLをご利用ください : https://ir.lib.hiroshima-u.ac.jp/00046552
| ファイル情報(添付) | |
| タイトル ( eng ) |
Mechanistic Insight on the Formation of GaN:ZnO Solid Solution from Zn–Ga Layered Double Hydroxide Using Urea as the Nitriding Agent
|
| 作成者 |
Hayashi Yuki
Yoshiyuki Risa
Uchiyama Tomoki
Nagata Noriyuki
Uchimoto Yoshiharu
Miyoshi Akinobu
Maeda Kazuhiko
|
| 収録物名 |
Inorganic Chemistry
|
| 巻 | 57 |
| 号 | 21 |
| 開始ページ | 13953 |
| 終了ページ | 13962 |
| 抄録 |
A solid solution of GaN and ZnO (GaN:ZnO) is promising as a photocatalyst for visible light-driven overall water splitting to produce H2. However, several obstacles still exist in the conventional preparation procedure of GaN:ZnO. For example, the atomic distributions of Zn and Ga are non-uniform in GaN:ZnO when a mixture of the metal oxides, i.e., Ga2O3 and ZnO, is used as a precursor. In addition, GaN:ZnO is generally prepared under harmful NH3 flow for long durations at high temperatures. Here, a facile synthesis of GaN:ZnO with homogeneous atomic composition via a simple and safe procedure is reported. A layered double hydroxide (LDH) containing Zn2+ and Ga3+ was used to increase the uniformity of the atomic distributions of Zn and Ga in GaN:ZnO. We employed urea as a nitriding agent instead of gaseous NH3 to increase the safety of the reaction. Through the optimization of reaction conditions such as heattreatment temperature and content of urea, single-phase GaN:ZnO was successfully obtained. In addition, the nitridation mechanism using urea was investigated in detail. NH3 released from the thermal decomposition of urea did not directly nitride the LDH precursor. X-ray absorption and infrared spectroscopies revealed that Zn(CN2)-like intermediate species were generated at the middle temperature range and Ga–N bonds formed at high temperature along with dissociation of CO and CO2.
|
| 内容記述 |
This file includes Supporting Information.
This work was supported by JSPS KAKENHI Grant Number JP16H06438, JP16H06441, JP17H05483, JP17H03392. This work was partly supported by the Center for Functional Nano Oxide at Hiroshima University. The synchrotron radiation experiments were performed at the BL01B1 beamline of SPring-8 with the approval of the Japan Synchrotron Radiation Research 32 Institute (JASRI) (Proposal No. 2017B1043 and 2018A1749).
|
| NDC分類 |
化学 [ 430 ]
|
| 言語 |
英語
|
| 資源タイプ | 学術雑誌論文 |
| 出版者 |
American Chemical Society
|
| 発行日 | 2018-11-05 |
| 権利情報 |
Copyright (c) 2018 American Chemical Society
This document is the Accepted Manuscript version of a Published Work that appeared in final form in 'Inorganic Chemistry', copyright c American Chemical Society after peer review and technical editing by the publisher. To access the final edited and published work see https://doi.org/10.1021/acs.inorgchem.8b02498.
This is not the published version. Please cite only the published version. この論文は出版社版でありません。引用の際には出版社版をご確認ご利用ください。
|
| 出版タイプ | Author’s Original（十分な品質であるとして、著者から正式な査読に提出される版） |
| アクセス権 | オープンアクセス |
| 収録物識別子 |
[ISSN] 0020-1669
[ISSN] 1520-510X
[DOI] 10.1021/acs.inorgchem.8b02498
[PMID] 30295474
|
| 備考 | Post-print version/PDF may be used in an institutional repository after an embargo period of 12 months. |