Fabricating hydrothermally robust ceramic membranes from amorphous yttrium-doped SiO2-ZrO2 composites

Lawal Sulaiman Oladipo

Takahashi Yuya

Moriyama Norihiro

Nagasawa Hiroki

Tsuru Toshinori

Kanezashi Masakoto

Journal of the European Ceramic Society

SiO2-ZrO2 ceramic composites are necessary for highly demanding separation processes. We demonstrated the efficacy of using yttrium doping to improve the hydrothermal stability of SiO2-ZrO2 composite-derived membranes. In long-term hydrothermal stability tests involving steam-N2 mixture permeation between 500–800 °C, N2 permeance for an undoped SiO2-ZrO2 membrane fabricated on an α-Al2O3 substrate decreased from 5.0 × 10−6 to 2.5 × 10−6 mol m−2 s−1 Pa−1 after 60 h between 500–700 °C and to 3.2 × 10−8 mol m−2 s−1 Pa−1 after 32 h at 800 °C. The yttrium-doped SiO2-ZrO2 membrane achieved a stable N2 permeance of 6.5 × 10−6 mol m−2 s−1 Pa−1 after 60 h between 500–700 °C, which decreased to 8.0 × 10−7 mol m−2 s−1 Pa−1 after 32 h at 800 °C. Microstructural analyses revealed that integrating yttrium into a SiO2-ZrO2 matrix suppressed segregation and aggregation rates of ZrO2 nanocrystals to form more stable microstructures.

Silica-zirconia

Yttrium doping

Hydrothermal stability

Amorphous

Tetragonal zirconia

Crystallization

英語

Elsevier

© 2024. This manuscript version is made available under the CC-BY-NC-ND 4.0 license https://creativecommons.org/licenses/by-nc-nd/4.0/

This is not the published version. Please cite only the published version.

この論文は出版社版ではありません。引用の際には出版社版をご確認、ご利用ください。

[DOI] https://doi.org/10.1016/j.jeurceramsoc.2024.116826 ～の異版である