Effect of Sodium Sulfate Activator on Compressive Strength and Hydration of Fly-Ash Cement Pastes

Phuong Trinh Bui

Ogawa Yuko

Kawai Kenji

Journal of Materials in Civil Engineering

In the study, the effect of 4% sodium sulfate (Na2SO4) as an activator on cement pastes with 0%, 20%, and 40% fly-ash replacements and a low water-to-cementitious materials ratio of 0.30 was investigated. The investigation was conducted to evaluate the effectiveness of the technique for the utilization of fly ash in developing sustainable concrete. The use of Na2SO4 decreased setting times of the fresh pastes and increased compressive strength of the hardened pastes up to 28 days irrespective of fly-ash replacement. The use decreased Ca(OH)2 content in the hardened pastes irrespective of fly-ash replacement. Meanwhile, it increased Ca(OH)2 consumption by the pozzolanic reaction of fly ash and content of calcium silicate and aluminate hydrates in the hardened fly-ash–cement pastes. Consequently, the use of Na2SO4 negatively affected cement hydration in the hardened cement pastes without fly ash, while it accelerated ettringite formation and pozzolanic reaction of fly ash in the hardened pastes.

Compressive strength

Hydration

Setting time

Thermal gravimetric analysis

X-ray diffraction

英語

American Society of Civil Engineers

This material may be downloaded for personal use only. Any other use requires prior permission of the American Society of Civil Engineers. This material may be found at https://doi.org/10.1061/(ASCE)MT.1943-5533.0003195.

This is not the published version. Please cite only the published version. この論文は出版社版ではありません。引用の際には出版社版をご確認、ご利用ください。

[ISSN] 0899-1561

[ISSN] 1943-5533

[DOI] 10.1061/(ASCE)MT.1943-5533.0003195

[DOI] https://doi.org/10.1061/(ASCE)MT.1943-5533.0003195