超臨界流体によるpoly(ethylene terephthalate)のマイクロセルラープラスチックス製造に関する基礎的研究 <論文>

A Fundamental Study for Microcellular Poly (ethylene telephtalate) Production Using Supercritical Fluids

佐藤 善之

近常 哲也

林 一成

滝嶌 繁樹

舛岡 弘勝

山本 博一

高杉 雅信

成形加工

Poly (ethylene terephthalate) (PET) foam was produced with a batch-wise method using carbon dioxide and nitrogen as physical blowing agents. Saturation pressure and temperature dependence of the foam structure was investigated. Solubility of the gases in PET and crystallinity of the PET induced by gas sorption were also investigated. PET foamed with CO2 at 323K and pressures higher than 10MPa had very fine cell structure (cell number density of 1012cm-3 and average cell diameter of 0.4μm). On the other hand, pressure dependence of the cell structure foamed with N2 was similar to results of amorphous polystyrene foam, whose cell structure became fine with increasing pressure. Volumetric expansivity of the PET+CO2 system rapidly decreased with increasing pressure, whereas that of the PET+N2 system gradually increased with increasing pressure. Cell structure foamed with CO2 became coarse with increasing saturation temperature. In the case of N2, saturation temperature dependence of cell structure was not observed at higher than 400K regardless of the solubility increase. These results suggested that cell structure and volumetric expansivity related not only to crystallinity but also to crystalline structure.

Cell structure , Volumetric expansivity , Poly (ethylene terephthalate) , Solubility , Crystallinity

化学工業 [ 570 ]

日本語

プラスチック成形加工学会

Copyright (c) 2004 社団法人 プラスチック成形加工学会

本文データはJournal@rchiveから複製したものである

[ISSN] 0915-4027

[DOI] 10.4325/seikeikakou.16.247

[NCID] AN10278882

[DOI] http://dx.doi.org/10.4325/seikeikakou.16.247