Enhancement of thermoelectric efficiency in type-VIII clathrate Ba8Ga16Sn30 by Al substitution for Ga

Deng Shukang

Saiga Yuta

Suekuni Koichiro

Takabatake Toshiro

Journal of Applied Physics

Single-crystalline samples of type-VIII clathrate Ba8Ga16-xAlxSn30 (0 <= x <= 12) were grown from Sn flux to characterize the structural and thermoelectric properties from 300 to 600 K. The lattice parameter increases by 0.5% as x is increased to 10.5 whose value is the solubility limit of Al. The Seebeck coefficients of all samples are largely negative and the absolute values increase to approximately 300 mu V/K on heating to 600 K. This large thermopower coexists with the metallic behavior in the electrical resistivity. The values of resistivity for 1 <= x <= 6 at 300 K are in the range 3.3-3.8 m Omega cm which is 70% of that for x=0. As a result, the power factor for x=4 and 6 has a rather large maximum of 1.83 x 10(-3) W/m K-2 at 480 K. The thermal conductivity stays at a low level of 0.72 W/mK up to 480 K, and the sample with x=6 reaches a ZT value of 1.2 at 500 K.

Physics [ 420 ]

eng

The American Institute of Physics

Copyright (c) 2010 American Institute of Physics

[ISSN] 0021-8979

[DOI] 10.1063/1.3490776

[NCID] AA00693547

[DOI] http://dx.doi.org/10.1063/1.3490776