High-Efficient and High-Speed Chromium Deposition in a Formic Acid Bath II. Influence of Chromium Ion Concentration in the Vicinity of the Cathode on the Appearance of Chromium Deposits
著者
安部 了介
松村 昌信
キーワード
High Current Efficiency
High Speed Deposition
Chromium Ion Concentration
Current Density
Rotating Disk Electrode
NDC
金属工学・鉱山工学
抄録(英)
A defect associated with the use of the Sargent bath, a widely-used device for chromium plating, is the substantially lower current efficiency of chromium, compared to that of other metals. It has been reported that the use of a formic acid bath leads to the production of amorphous-structured chromium deposits with a higher current efficiency. However, it is difficult to use this process commercially, because of difficulties involved in maintaining the bath. In this paper, the concentration of Cr3+ ion in the vicinity of the cathode in a formic acid bath was estimated from the current density, the aging time of the bath and the rotating speed of the rotating disk electrode (RDE) apparatus. The results show that Cr3+ concentration plays the most important role in determining the appearance of the deposited metal. The effect of formic acid and sulfuric acid on the chromium deposit was investigated, and the optimum Cr3+ concentration in the vicinity of the cathode on the chromium deposition process was determined. Taking these results into account, the conditions required for obtaining a bright deposit with a high current efficiency at a high deposition rate could be predicted, resulting in a bright deposit with a current efficiency of 64.8-0x1.fe3a0000008p+0t a deposition rate of 17.1μm/min.
掲載誌名
表面技術
55巻
2号
開始ページ
139
終了ページ
144
出版年月日
2004-02-01
出版者
表面技術協会
ISSN
0915-1869
NCID
出版者DOI
言語
日本語
NII資源タイプ
学術雑誌論文
広大資料タイプ
学術雑誌論文
DCMIタイプ
text
フォーマット
application/pdf
著者版フラグ
publisher
権利情報
本文データは学協会の許諾に基づきJ-STAGEから複製したものである
Copyright (c) 2005 (社)表面技術協会
関連情報URL
部局名
工学研究科