Lithium nitride for reversible hydrogen storage
JAllCompd_365_1-2_271.pdf 545 KB
Lithium amide, -imide, -hydride, -nitride
In this paper, we examined the basic properties in the 1:1 mixture of lithium amide LiNH2 and lithium hydride LiH as a candidate of reversible hydrogen storage materials. The thermal desorption mass spectra of the ball milled mixture without any catalysts indicated that hydrogen H2 is released in temperature range from 180 to 400 ℃ with emitting a considerable amount of ammonia NH3. On the other hand, the ball milled mixture containing a small amount of TiCl3 as a catalyst showed the most superior hydrogen storage properties among the 1:1 mixtures with a small amount of catalysts, Ni, Fe, Co metals and TiCl3 (1 mol.%). That is, the product desorbs a large amount of hydrogen (~5.5 wt.%) in the temperature from 150 to 250 ℃ under the condition of a heating rate of 5 ℃/min, but it does not desorb ammonia at all within our experimental accuracy. In addition, we confirmed that the product shows an excellent cycle retention with an effective hydrogen capacity of more than 5 wt.% and a high reaction rate until at least 3 cycles.
Journal of Alloys and Compounds
|date of issued||
Copyright (c) 2003 Elsevier B.V.
Natural Science Center for Basic Research and Development
Institute for Advanced Materials Research
Last 12 months's access : ? times
Last 12 months's DL: ? times
This month's access: ? times
This month's DL: ? times