Enhanced visible-light photocatalytic activity of anatase-rutile mixed-phase nano-size powder given by high-temperature heat treatment
Royal Society Open Science 7 巻
191539- 頁
2020-01-15 発行
アクセス数 : 130 件
ダウンロード数 : 50 件
今月のアクセス数 : 8 件
今月のダウンロード数 : 4 件
この文献の参照には次のURLをご利用ください : https://ir.lib.hiroshima-u.ac.jp/00053538
| ファイル情報(添付) | |
| タイトル ( eng ) |
Enhanced visible-light photocatalytic activity of anatase-rutile mixed-phase nano-size powder given by high-temperature heat treatment
|
| 作成者 |
Ishigaki Takamasa
Nakada Yusuke
Uchikoshi Tetsuo
Tsujimoto Yoshihiro
Isobe Masaaki
Ogata Hironori
Zhang Chenning
Hao Dong
|
| 収録物名 |
Royal Society Open Science
|
| 巻 | 7 |
| 開始ページ | 191539 |
| 抄録 |
Nano-size EVONIK AEROXIDE® P25 titanium dioxide, TiO2, powder was heat-treated at temperatures, 700–900°C, in air. An X-ray diffraction study showed that the P25 powder is composed of approximately 20 and approximately 80 mass% of rutile and anatase phases, respectively. It was also shown that the transformation from anatase to rutile induced by hightemperature heat treatment was almost completed at 750°C, whereas a small amount (less than 3 mass%) of anatase phase was still left even in the powder heat-treated at 900°C. The transformation behaviour was consistent with results obtained by Raman scattering spectroscopy. Raman experiments also indicated that high-temperature heating induced the formation of oxide ion vacancies. Powders were dispersed in methyl orange (MO) aqueous solution, and the bleach rate of MO was measured to evaluate photocatalytic activity under ultraviolet (UV)- and visible-light irradiation. After the heat treatment, the UV-light photocatalytic performance sharply deteriorated. Interestingly, visible-light photocatalytic activity was enhanced by high-temperature heating and reached the highest performance for an 800°C-heated sample, indicating that the P25 powder obtained high visible-light photocatalytic performance after heat treatment. Even after 900°C heat treatment, the photocatalytic performance was higher than that of as-received powder. Enhancement of photocatalytic activities was discussed in relation to visible light absorption and charge carrier transfer.
|
| 著者キーワード |
titanium oxide
nano-size powder
phase transformation
mixed-phase
photocatalyst
|
| 内容記述 |
T.I., H.O. and D.H. were supported by a programme, the Strategic Research Foundation at Private Universities, grant no. S1311023, from Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan.
|
| 言語 |
英語
|
| 資源タイプ | 学術雑誌論文 |
| 出版者 |
Royal Society of Chemistry
|
| 発行日 | 2020-01-15 |
| 権利情報 |
© 2020 The Authors. Published by the Royal Society under the terms of the Creative Commons Attribution License http://creativecommons.org/licenses/by/4.0/, which permits unrestricted use, provided the original author and source are credited.
|
| 出版タイプ | Version of Record（出版社版。早期公開を含む） |
| アクセス権 | オープンアクセス |
| 収録物識別子 |
[ISSN] 2054-5703
[DOI] 10.1098/rsos.191539
[DOI] http://dx.doi.org/10.1098/rsos.191539
|