キーワード
Hydrogen storage materials
Gas-solid reactions
High-energy ball milling
Mechanochemical synthesis
Thermal analysis
NDC
物理学
抄録(英)
Isothermal hydrogen absorption properties of the ball milled mixture of 3Mg(NH2)2 and 8LiH after dehydrogenation at 200 °C under high vacuum were investigated at two different temperatures of 150 and 200 °C. The pressure –composition isotherm (PCT) curve at 200 °C revealed a two-plateaus-like behavior, while the PCT curve at 150 °C showed a single-plateau-like behavior. The hydrogenated phases were composed of LiH and Mg(NH2)2 under 9 MPa at 200 °C, while those were observed as mixed phases of LiH and LiNH2 at 150 °C without any trace of Mg(NH2)2 in XRD measurements. These results indicate that there are 2 step hydrogenation processes corresponding to high and low pressures at 200 °C, but the kinetics at 150 °C is too slow to proceed with the second hydrogenating step at high pressure region.
掲載誌名
Journal of Alloys and Compounds
400巻
1-2号
開始ページ
245
終了ページ
248
出版年月日
2005-09-01
出版者
Elsevier B.V.
ISSN
0925-8388
NCID
出版者DOI
言語
英語
NII資源タイプ
学術雑誌論文
広大資料タイプ
学術雑誌論文
DCMIタイプ
text
フォーマット
application/pdf
著者版フラグ
author
権利情報
Copyright (c) 2005 Elsevier B.V.
関連情報URL
部局名
自然科学研究支援開発センター
先進機能物質研究センター